PDMDAAC改性膨潤土的制備及吸附性能

作　　者：王大衛 邵紅 劉相龍 丁佳

WANG Da-wei,SHAO Hong,LIU Xiang-long,DING Jia （ Shenyang University of Chemical Technology, Shenyang 110142, China）

機構地區：沈陽化工大學環境與安全工程學院,遼寧沈陽110142

出　　處：《沈陽化工大學學報》 2015年第29卷第1期 18-22頁,共5頁

Journal of Shenyang Institute of Chemical Technolgy

摘　　要：以膨潤土為原料,聚二甲基二烯丙基氯化銨（PDMDAAC）為改性劑,制備一種新型水處理劑——PDMDAAC有機改性膨潤土.處理苯胺模擬廢水,以苯胺去除率為考核指標,確定最佳制備條件為：膨潤土中改性劑的量為800 g/kg,土液比為150 g/L,攪拌時間為60 min,溫度為20℃,苯胺去除率可達80%.對改性膨潤土進行X射線衍射（XRD）,掃描電鏡（SEM）和紅外光譜（FTIR）分析,結果表明：PDMDAAC并未進入膨潤土層間,只是負載于膨潤土表面,有效增大了膨潤土的吸附能力。

Using bentonite as rawmaterial and PDMDAAC as modifierprepared a newtype of water treatment agent—PDMDAAC organic modified bentonite. With treating simulated anilinewastewater,aniline removal rate was as evaluation index to determine the optimum conditions as follows： bentonite per kilogram modifier was 800 g / kg,soil liquid ratio was 150 g / L,stirring time was 60 min,the mixingtemperature was 20 ℃,aniline removal was up to 80 %. Modification of bentonite by X ray diffraction（ XRD）,scanning electron microscopy（ SEM） and infrared spectroscopy（ FT-IR） analysis,the results showthat,PDMDAAC did not enter into the bentonite interlayer,just loaded on the surface in the bentonite,effectively increased the adsorption capacity of bentonite.

關鍵詞：改性膨潤土 聚二甲基二烯丙基氯化銨 模擬苯胺廢水 去除率

modified bentonites ; PDM DAAC ; simulated aniline wastewater ; removal rate ;

分類號：F703.1 [經濟 > 貿易經濟]

部分內容：

解決水體污染的關鍵問題在于水處理技術的發展，其中對于水處理劑的要求尤為關鍵，不僅要求對水體污染處理效果好，還要求對水體水質沒有二次污染，同時，還要求有較高的經濟效益．苯胺類化合物微溶于水，易溶于乙醇、乙醚及丙酮．常用于染料、藥物制造及橡膠、塑料、油漆等的原料，對生物有毒性作用，它可通過呼吸道、消化道、皮膚進入生物體內，不僅能使氧合血紅蛋白變為高鐵血紅蛋白從而降低血液的載氧能力，使組織細胞缺氧而窒息，影響神經系統的功能，而且苯胺類化合物還具有致癌作用．因而苯胺類常作為制藥、印染等行業污染物排放控制的重要指標．膨潤土是一種儲量豐富、價格低廉的天然黏土礦物材料，因具有表面吸附作用、層間陽離子交換能力、孔道過濾功能和特殊納米結構．效應等特性，廣泛應用于醫藥、鉆井、石油、化工、輕工、紡織、造紙、環境治理等領域。膨潤土的改性及其在環境污染控制和修復中的應用已成為國內外研究熱點之一。

本文研究的聚二甲基二烯丙基氯化銨(PDMDAAC)是陽離子高分子有機絮凝劑，正電荷密度高，水溶性好，高效無毒．將其作為改性劑，對膨潤土進行改性，用其處理含苯胺廢水，能使廢水的苯胺大幅度降低，殘留物不會造成二次污染 ]．為在環境污染治理中的新型絮凝劑開發與利用提供了一種新的思路．

瀏覽全文